Item | SilverSol | Silver Powder/ Nitrate |
---|---|---|
Bonding onto Carbon | Permanently bonded onto carbon | Loosely bonded onto carbon |
Characteristic of Product | Liquid | Powder |
Cost of Production | Low (very economical) | High cost |
Coating / Absorption | 100% – Evenly Coated | Not evenly mixed / coated |
Effectiveness over long period of usage | Permanent / Life Long | Lost effectiveness after long period of usage |
Silver Content | 10-50,000ppm depending on the application / usage | 1-2% silver powder/ nitrate is added for coating (ppm-varied) |
BSS | USS | ||
Sieve No. | mm | Sieve No. | mm |
1/4 | 6.7 | 3 | 6.3 |
3/16 | 4.75 | 4 | 4.75 |
5 | 3.35 | 6 | 3.35 |
6 | 2.8 | 7 | 2.8 |
7 | 2.36 | 8 | 2.36 |
8 | 2 | 10 | 2 |
10 | 1.7 | 12 | 1.7 |
12 | 1.4 | 14 | 1.18 |
14 | 1.18 | 18 | 0.85 |
18 | 0.85 | 20 | 1.7 |
22 | 0.71 | 25 | 0.71 |
25 | 0.6 | 30 | 0.6 |
30 | 0.5 | 35 | 0.5 |
36 | 0.425 | 40 | 0.425 |
44 | 0.355 | 50 | 0.6 |
52 | 0.3 | 60 | 0.3 |
72 | 0.212 | 70 | 0.212 |
100 | 0.15 | 100 | 0.15 |
200 | 0.075 | 200 | 0.075 |
350 | 0.045 | 325 | 0.045 |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 55 % | ASTM D37-88 |
Apparent Density | 0.42 to 0.48 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 95% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | < 5% | ASTM D2866-83 |
pH Value | 9.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+12 | (+1.70mm) | >5% |
-12+30 | (-1.70mm+0.60mm) | >90% |
-30 | (-0.60mm) | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 55% | ASTM D3467-88 |
Apparent Density | 0.42 to 0.48 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 95% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | <3% | ASTM D2866-83 |
pH Value | 9.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+14 | (+1.40mm) | >5% |
-14+10 | (-1.40mm+0.42mm) | >90% |
-4 | (-0.42mm) | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 55% | ASTM D3467-88 |
Apparent Density | 0.42 to 0.51 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 95% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | < 3% | ASTM D2866-83 |
pH Value | 9.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+12 | (+1.70mm) | >5% |
-12+30 | (-1.70mm+0.60mm) | >90% |
-30 | (-0.60mm) | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 55% | ASTM D2854-88 |
Apparent Density | 0.42 to 0.51 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 95% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | < 4% | ASTM D2866-83 |
pH Value | 8 to 10.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+8 | (+2.36mm) | >5% |
-12+30 | (-2.36mm+0.60mm) | >90% |
-30 | (-0.60mm) | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 60% | ASTM D3467-88 |
Apparent Density | 0.78 to 0.82 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 95% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | < 3% | ASTM D2866-83 |
pH Value | 9.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+4 | - | >5% |
-4+8 | - | >90% |
-8 | - | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 60% | ASTM D3467-88 |
Apparent Density | 0.78 to 0.82 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 95% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | <5% | ASTM D2866-83 |
pH Value | 9.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+8 | (+4.75mm) | >5% |
-4+8 | (-4.75mm+2.36mm | >90% |
-8 | (-2.36mm) | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1000 to 1100 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 50 to 55% | ASTM D3467-88 |
Apparent Density | 0.45 to 0.52 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 98% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | <5% | ASTM D2866-83 |
pH Value | 10 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+4 | (+4.75mm) | >5% |
-4+8 | (-4.75mm+2.36mm | >90% |
-8 | (-2.36mm) | <5% |
Typical Analysis | Method of Analysis | |
---|---|---|
Iodine No. | 1200 to 1300 mg/g | ASTM D4607-86 |
CTC (CCL4) Activity | 60 to 65% | ASTM D3467-88 |
Apparent Density | 0.47 to 0.51 g/cc | ASTM D2854-89 |
Ball Pan Hardness | 98% Min | ASTM D3820-79 |
Moisture Content | < 5% | ASTM D2867-91 |
Ash Content | < 5% | ASTM D2866-83 |
pH Value | 10.5 | JIS K1470 |
PARCTICLE SIZE DISTRIBUTION | ASTM D2862-82 | |
Mesh | ||
+4 | (+4.75mm) | >5% |
-4+8 | (-4.5mm+2.36mm | >90% |
-8 | (-2.36mm) | <5% |